- Mode I interlaminar fracture mechanics of unidirectionally reinforced carbon/nylon laminates.
- 1ホウコウ カーボン ナイロン セキソウバン ノ モード I ソウカン ハカイ
この論文をさがす
抄録
Mode I interlaminar fracture toughness of CFRP is evaluated using DCB (Double Cantilever Beam) specimens. Unidirectionally reinforced carbon/nylon laminates were used for the test. The fracture toughness value, Gc, was obtained by the area method, compliance method and nonlinear analysis. The Gc of 2 mm-thick specimen is 10-12 times larger than that of an epoxy specimen. However, in case of an 8 mm-thick specimen, voids and fiber-bridging are observed, and the fracture mechanism is complicated. Acoustic emission (AE) was also measured during the compliance test. It is shown that the viscoelastic and plastic effects should be considered in studing the fracture mechanism.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 53 (496), 2386-2393, 1987
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204477026688
-
- NII論文ID
- 110002373659
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 3162972
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可