ＳＵＳ３１６Ｌ平滑材の１０｀７´回時間強度に及ぼす水素ガス環境の影響（微視的疲労き裂の挙動に注目して）

DOI Web Site Web Site 被引用文献3件 参考文献25件

書誌事項

タイトル別名
  • Effects of Hydrogen Gas Environment on the Fatigue Strength at 107 cycles in the Plain Specimens of Type 316L Stainless Steel (A Report Focusing on the Behavior of Micro Fatigue Crack)
  • SUS316L ヘイカツザイ ノ 10 7 カイ ジカン キョウド ニ オヨボス スイソ ガス カンキョウ ノ エイキョウ ビシテキ ヒロウ キレツ ノ キョドウ ニ チュウモクシテ
  • A Report Focusing on the Behavior of Micro Fatigue Crack
  • 微視的疲労き裂の挙動に注目して

この論文をさがす

抄録

In order to investigate the hydrogen effect on the fatigue strength at 107 cycles of type 316L stainless steel, the rotating bending fatigue tests in atmospheric air and the plane bending fatigue tests in 1 MPa dry hydrogen gas and in air were carried out. The observed fatigue behavior showed that the fatigue strength at 107 cycles in both environments is determined by the non-propagation of fatigue crack of the order of the grain size. And, the strength at 107 cycles in hydrogen is slightly higher than that in air. In the region of long fatigue life, the fatigue life in hydrogen is longer than that in air, which is mainly caused by the longer crack initiation life in hydrogen. The crack propagation life in hydrogen is shorter than that in air, but has only a small ratio to the fatigue life in this region.

収録刊行物

被引用文献 (3)*注記

もっと見る

参考文献 (25)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ