- Characterization of the sub-critical crack growth of low alloy steels in a hydrogen environment by means of a acoustic-emission.
- スイソ ガス カンキョウカ デ ノ テイゴウキン コウ ノ キレツ シンテン
この論文をさがす
抄録
Slow strain rate tests (SSRT) have been carried out using precracked compact tension specimens of low alloy steels in purified hydrogen gas at ambient temperature. By the use of elastic-plastic fracture mechanics parameters, the influence of hydrogen gas on sub-critical crack growth has been investigated in terms of the J-value at the onset of crack extension and also from a view point of fracture modes. Acoustic-Emission (AE) during the SSRT tests has been monitored to clarify the cracking behavior in hydrogen gas and by mechanical tearing. In a hydrogen gas environment, it is clearly shown that a crack initiates and propagates in a quasi-cleavage manner until applied the J value reaches J1c and after that the fracture mode changes to mixture of ductile dimple and quasi-cleavage. This result suggests that mechanical tearing occurs at J-values greater than J1c even in a hydrogen environment. In SA 533 B steels, the AE activity showed two energy peaks with respect to loading levels, whose origins are attributable to the onset of quasi-cleavage fracturing caused by the environment and to the onset of mechanical tearing.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 54 (497), 50-56, 1988
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204479045632
-
- NII論文ID
- 110002377480
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 3170772
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可