Fracture Mechanism in Fatigue of Ni-Base Superalloy Inconel 718 at Elevated Temperatures
-
- KAWAGOISHI Norio
- Department of Mechanical Engineering, Kagoshima University
-
- YAN Nu
- 鹿児島大学大学院理工学研究科
-
- GOTO Masahiro
- 大分大学工学部
-
- CHEN Qiang
- 高知工業高等専門学校機械工学科
-
- WANG Qingyuan
- 四川大学工学部
-
- OHZONO Yoshihisa
- 鹿児島大学機器分析センター
Bibliographic Information
- Other Title
-
- Ni基超合金インコネル718の中高温疲労における破壊機構
- Niキ チョウゴウキン インコネル 718 ノ チュウコウオン ヒロウ ニ オケル ハカイ キコウ
Search this article
Abstract
In order to investigate the fracture mechanism in fatigue of Ni-base superalloy at elevated temperatures, rotating bending fatigue tests were carried out for Inconel 718 at 500°C and 600°C up to 108 cycles. At both temperatures, fracture occurred from a subsurface of the specimen in long life region, though the origin of fracture was the specimen surface in short life region. Consequently, S-N curves showed a two-step shape in elevated temperature tests. Although a surface crack was observed similar to the result at room temperature even in long life region at elevated temperatures, the surface crack stopped propagating. In this case, interganular cracks were observed at an origin of subsurface fracture. The subsurface damage was initiated at the early stage of fatigue life.
Journal
-
- TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
-
TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A 71 (709), 1226-1233, 2005
The Japan Society of Mechanical Engineers
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001204479085824
-
- NII Article ID
- 110004999072
-
- NII Book ID
- AN0018742X
-
- COI
- 1:CAS:528:DC%2BD2MXht1GmtbfJ
-
- ISSN
- 18848338
- 03875008
- http://id.crossref.org/issn/03875008
-
- HANDLE
- 10559/13901
-
- NDL BIB ID
- 7490038
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- IRDB
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed