- The rotary bending fatigue of a eutectoid steel. (1st report Effects of surface finish and defects on fatigue limit)
- キョウセキ コウ ノ コウ サイクル カイテン マゲ ヒロウ 1 ヒロウ キョ
この論文をさがす
抄録
To examine the effects of the surface finish and defects on fatigue limit, specimens differently finished, i. e., sand paper (Grade #600, #80) finish and electrolytic polish, were prepared. Moreover, to simulate surface defects, a small artificial hole of which diameter is varied from 40 to 200 μm is introduced on the specimen surface. Both as-received and annealed specimens were applied so as to extract the effect of the work-hardened surface layer on the fatigue limit. Through examination of the fatigue limit and ten non-propagating crack the following results are obtained: (1) the surface roughness slightly influences the fatigue limit, while the work-hardened surface layer has a primary effect on the fatigue limit. (2) An increase in the diameter of the small hole decreases the fatigue limit and results in the prolongation of the non-propagating crack. (3) For the non-propagating crack, the threshold stress intensity factor range ΔKth decreases with a decrease in the crack length.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 53 (487), 401-409, 1987
一般社団法人 日本機械学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204479207296
-
- NII論文ID
- 110002377202
-
- NII書誌ID
- AN0018742X
-
- ISSN
- 18848338
- 03875008
- http://id.crossref.org/issn/00290270
-
- NDL書誌ID
- 3125893
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可