- The Tribological and Fatigue Properties of Steel modified by Hybrid Surface Modification Combining Super Rapid Induction Heating and Quenching with DLC Coating
- チョウキュウソク コウシュウハ ヤキイレ ト DLC ヒマク ニ ヨル フクゴウ ヒョウメン カイシツコウ ノ マサツ マモウ トクセイ オヨビ ヒロウ トクセイ
この論文をさがす
抄録
In recent years, with the background of weight saving and downsizing in machines and devices, it is important subject to downscale mechanical parts which are contained in them. So in this study, in order to achieve power transmission parts like a compact gearwheel which indicates high performance properties, hybrid surface modification was performed by combining Super Rapid Induction Heating and Quenching (SRIQ) which creates high fatigue strength and Diamond Like Carbon (DLC) coating which are well known for their high hardness, low friction and excellent wear resistance. And, in order to prevent the base material from decreasing its fatigue strength, DLC was coated by using Unbalanced Magnetron Sputtering (UBMS) method which can coat at low temperature. Rotational bending fatigue tests and friction-wear tests were carried out. It was clear that it is possible to keep high fatigue strength and to create excellent tribological properties at specimen surface by performed hybrid surface modification. Furthermore, it is possible to prevent increase in handling process because tempering process after quenching can be performed by heat process during DLC coating process.
収録刊行物
-
- 日本機械学会論文集A編
-
日本機械学会論文集A編 73 (731), 803-808, 2007
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204479282816
-
- NII論文ID
- 110006367683
-
- NII書誌ID
- AN0018742X
-
- COI
- 1:CAS:528:DC%2BD2sXhtFSgurzP
-
- ISSN
- 18848338
- 03875008
-
- NDL書誌ID
- 8901981
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可