Failure behavior of fine powder beds by upward air flow was investigated experimentally with a two-dimensional column to clarify the mechanism of agglomerate formation in the bed. To analyze the crack formation process the stress distributions in beds of uniform structure were calculated with the finite element method based on an elastic model.<BR>In any case the first step of the failure process was crack formation by the pressure gradient due to air throughflow in the bed. However, the second step depended on bed conditions.<BR>In beds of cohesionless powders, the particles around cracks were easily agitated and locally fluidized by the penetrating air. Similar situations were observed in the case of cohesive powders if the bed was loosely packed. In beds of densely packed cohesive powders no agitation and fluidization were created immediately.<BR>Primary cracks were formed at the bed bottom on wall sides. The stress distribution prediction by the finite element analysis with the elastic bed model provided satisfactory implications for the observed crack formation.
収録刊行物
-
- 化学工学論文集
-
化学工学論文集 20 (3), 387-396, 1994
公益社団法人 化学工学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204510687616
-
- NII論文ID
- 130000866089
-
- NII書誌ID
- AN00037234
-
- ISSN
- 13499203
- 0386216X
-
- NDL書誌ID
- 3873978
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可