- Release Rate Measurement of Antifoulant from Hull Paint of Ship
- ジッセン ニ ヨル センテイ トリョウ カラノ ボウオ ブツシツ ノ ヨウシュツ ソクド ソクテイ
この論文をさがす
説明
In order to measure the release rate of anti-foulant from a ship's hull paint, paint specimens were mounted on a ship and their loss of thickness after sailing was measured. Specimens were prepared by coating conventional paints onto steel plates. The major anti-foulants were cuprous oxide and copper pyrithione. They were mounted on bilge keel of a training ship. After sailing, the specimens were collected periodically and the coating thickness measured. The average release rate, estimated from the thickness differences, varied from 11 to 40 μg/cm2/day. The release rate increased throughout the voyage when both average sailing speed and water temperature remained high. Observations of the cross section of a coating revealed formation of a skeleton layer near the surface where anti-fouling substances had leached out. Obtained release rates and the observed coating structures, are similar to those in laboratory tests which used rotating cylinders.
収録刊行物
-
- マリンエンジニアリング
-
マリンエンジニアリング 44 (2), 292-297, 2009
公益社団法人 日本マリンエンジニアリング学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204572962176
-
- NII論文ID
- 10024788285
-
- NII書誌ID
- AA11505252
-
- ISSN
- 18843778
- 13461427
-
- NDL書誌ID
- 10185436
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可