- Effects of Crystallinity on Dielectric Properties of Poly (L-lactide)
- Lガタ ポリ ニュウサン ノ ケッショウカド ガ ユウデン トクセイ ニ アタエル エイキョウ
この論文をさがす
抄録
Poly (L-lactide) (PLLA) is attracting much attention as a biodegradable polymer. In this paper, effects of crystallinity on dielectric properties of PLLA are studied. At 80°C, which is above the glass transition temperature (about 60°C), the conductivity increases with a decrease in crystallinity. A thermally stimulated polarization current (TSPC) peak, which seems to be due to segmental-mode relaxation, appears in all the samples at temperatures around 65 to 70°C, and it becomes smaller as the crystallinity increases. All the samples show two thermally stimulated depolarization current (TSDC) peaks at around 65°C and around 90 to 100°C. The lower-temperature peak seems to be due to the segmental-mode relaxation, while the other due to the normal-mode relaxation. Moreover, all the samples show a drastic increase in the real part of complex permittivity (εr') and a peak in its imaginary part (εr”) at frequencies from 10-1 to 104 Hz, depending on the measurement temperature. The crystallinity dependencies of the two parts are similar to those of the TSPC and TSDC peaks around 65 to 70°C. Therefore, the increase in εr' and the peak in εr” are ascribable to the segmental-mode relaxation.
収録刊行物
-
- 電気学会論文誌. A
-
電気学会論文誌. A 129 (4), 217-222, 2009
一般社団法人 電気学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204594209920
-
- NII論文ID
- 10024772955
-
- NII書誌ID
- AN10136312
-
- BIBCODE
- 2009IJTFM.129..217H
-
- ISSN
- 13475533
- 03854205
-
- NDL書誌ID
- 10250371
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可