  • Diamond-Like Carbon Film Produced by Vacuum Arc Deposition Technique and its Surface Appearance
  • シンクウ アーク ジョウチャクホウ オ モチイタ ダイヤモンド ライク カーボ
  • Diamond‐like carbon film produced by vacuum arc deposition technique and its surface appearance

この論文をさがす

説明

Diamond-like carbon (DLC) films are deposited in a dc vacuum arc plasma with a graphite cathode. The arc current, the flow rate of hydrogen gas and the pressure are 50A, 10ml/min and O.05Pa, respectively. The substrate materials are Si (111), soda-glass and Mo. Process parameters are deposition time (3-30min). The films are analyzed by the laser raman spectroscopy and surface appearance of the films are observed with an optical microscope.<br>The results are as follows: (1) The films deposited under these conditions have diamond-like carbon structure. (2) The films deposited for 3min on Si or Mo and for 5min on glass wrinkle on the substrates. (3) The films deposited for more than 10min on Si and for more than 15min on glass crack and flake off the substrates. (4) The films deposited for more than 10min on Mo plainly stick on the substrate without any wrinkles or flakes.<br>It is found that plain DLC films are able to be produced by the vacuum arc deposition method if the deposition time is appropriately selected, while never by the conventional plasma CVD method.

収録刊行物

被引用文献 (13)*注記

もっと見る

参考文献 (13)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ