Magnetoresistance Effect of Granular Films Employing Co2FeAl0.5Si0.5 Alloy
-
- Sato Kazunori
- Mie University
-
- Fujiwara Yuji
- Mie University
-
- Kato Takeshi
- Nagoya University
-
- Jimbo Mutsuko
- Daido University
-
- Kobayashi Tadashi
- Mie University
Bibliographic Information
- Other Title
-
- Co2FeAl0.5Si0.5合金を用いたグラニュラー薄膜の磁気抵抗効果
- Co2FeAl0 5Si0 5 ゴウキン オ モチイタ グラニュラー ハクマク ノ ジキ テイコウ コウカ
Search this article
Abstract
Magnetoresistance (MR) effects and electroric structure were investigated for granular films employing Co2FeAl0.5Si0.5 (CFAS) alloy. CFAS-MgO granular films showed a maximum MR ratio of approximately 4.8 %. It was however recognized that the surface of CFAS granules was slightly oxidized due to the low formation energy of MgO matrix. By utilizing MgF2 matrix, the MR ratio increased to approximately 6.5 %. After annealing at 200°C, the MR ratio increased slightly. It was thought that the L21 ordered structure was not obtained due to the low annealing temperature. Further annealing at high temperature is required to obtain L21 ordered CFAS granules.
Journal
-
- IEEJ Transactions on Fundamentals and Materials
-
IEEJ Transactions on Fundamentals and Materials 130 (7), 626-630, 2010
The Institute of Electrical Engineers of Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001204599420416
-
- NII Article ID
- 10026865145
-
- NII Book ID
- AN10136312
-
- ISSN
- 13475533
- 03854205
-
- NDL BIB ID
- 10740727
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed