- Cryocooler with Magnetic Regenerator Materials Review Article. The Magnetic Field Influences on the Regenerator Materials and the Proposal of the New Antiferromagnetic Material Ho2Al.
説明
Many rare-earth compounds have been studied to attain a large volumetric specific heat in cryogenic temperatures and to aim at developing regenerator materials for a regenerative refrigerator. The magnetic specific heats of these materials are so large that the performance of refrigeration for a Gifford-McMahon refrigerator has been greatly improved and helium temperatures have been attained. In an application for the superconducting magnet, the refrigerator must be operated under the magnetic field. So, magnetic regenerator materials are required to be free from the influences of the magnetic field. In this paper, the magnetic field influences on the regenerator materials Er3Ni, ErNi and Er3Co, are discussed and Ho2Al is proposed as a new regenerator material which is free from the influence of the magnetic field. The magnetic properties of Er3Ni, ErNi and Er3Co were investigated at cryogenic temperatures in a magnetic field of up to 5 Tesla. The magnetic forces were evaluated for these materials under the magnetic field using the magnetic moment values deduced from the magnetization measurements. The magnetic forces for ferromagnetic materials such as the ErNi and Er3Co turned out to be one order of magnitude larger than that for antiferromagnetic material Er3Ni. It was confirmed that the antiferromagnetic material is superior to the ferromagnetic one in case of the exposure to the large magnetic field and large gradient of the field. Further, new antiferromagnetic regenerator materials were searched and Ho2Al was found to have a volumetric specific heat as large as Er3Co in the temperature range from 10 to 16K.
収録刊行物
-
- 低温工学
-
低温工学 31 (4), 182-189, 1996
公益社団法人 低温工学・超電導学会 (旧 社団法人 低温工学協会)
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204614874880
-
- NII論文ID
- 130003673070
-
- ISSN
- 18800408
- 03892441
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可