- Effects of carbon content and heat treatment on fatigue life of high strength Cr-Mo steel charged with hydrogen
- スイソ テンカ シタ コウキョウド Cr-Moコウ ノ ヒロウ ジュミョウ エ ノ タンソ ガンユウリョウ ト ネツ ショリ ノ エイキョウ
この論文をさがす
抄録
Hydrogen susceptibility in fatigue life has been examined using commercial JIS SCM420 steel. The effects of carbon content, austenitizing temperature and tempering temperature have been explored in comparison with JIS SCM435 steel that was given the standard heat treatment. Discussion has been made with the information of hydrogen thermal desorption spectroscopy (TDS) and appearance of carbide precipitation. When the tensile strength of SCM420 steel is adjusted to the normally heat treated SCM435 steel by combining higher austenitizing temperature and lower tempering temperature, fatigue life ratio that is the fatigue life of hydrogen pre-charged specimen divided by that of non-charged one stays almost unaffected. When tempering is further lowered to 448K, the tensile strength reaches almost 1500MPa, but the drop in fatigue life ratio is minute. One of the reasons is the suppressed phosphorus segregation along austenite grain boundary that is brought about by elevating the austenitizing temperature. The other is especially for 448K tempering. It is the reduced hydrogen segregation along prior austenite grain boundary, as the results of scarce carbide precipitation along it.
収録刊行物
-
- 圧力技術
-
圧力技術 51 (2), 45-52, 2013
一般社団法人 日本高圧力技術協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204616733824
-
- NII論文ID
- 10031163140
-
- NII書誌ID
- AN00011762
-
- ISSN
- 13479598
- 03870154
-
- NDL書誌ID
- 024648323
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可