Strength of 6191 aluminum bronze stud joints by friction welding
-
- OCHI Hiizu
- Osaka Institute of Technology Incubation Laboratory
-
- KAWAI Gosaku
- Osaka Sangyo University Faculty of Engineering
-
- MORIKAWA Katsuyoshi
- Osaka Sangyo University Junior College
-
- SAKURAI Keizo
- Osaka Sangyo University Faculty of Engineering
-
- ISSIKI Yoshihiro
- Setsunan University Faculty of Science and Engineering
Bibliographic Information
- Other Title
-
- 摩擦圧接を用いた6191アルミニウム青銅スタッド継手の強度
- マサツ アッセツ オ モチイタ 6191 アルミニウム セイドウ スタッド ツギテ ノ キョウド
Search this article
Abstract
Stud joints of C6191 aluminum bronze were friction welded and its joint strength was examined. A hardened stir zone formed at the weld interface and its width increased with a friction time. In the tensile testing, since all friction welded joints fractured in the plate side, friction weldability of C6191 stud joints was good. Contrary, arc stud welded joints fractured at the weld zone and there were blowholes. In the bending testing, friction welded joints were fractured near the weld zone at bending angle of about 5°. In the fatigue testing, friction welded joints fractured near the weld zone and the fatigue limits of joints were 90-115MPa.
Journal
-
- Journal of High Pressure Institute of Japan
-
Journal of High Pressure Institute of Japan 49 (5), 225-231, 2011
HIGH PRESSURE INSTITUTE OF JAPN(HPI)
- Tweet
Details 詳細情報について
-
- CRID
- 1390001204616750336
-
- NII Article ID
- 130004446887
- 10029695693
-
- NII Book ID
- AN00011762
-
- ISSN
- 13479598
- 03870154
-
- NDL BIB ID
- 11267576
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- CiNii Articles
-
- Abstract License Flag
- Disallowed