Mode II Fracture Toughness of CFRP Adhesive Bonded Structure at Cryogenic Temperature
-
- YOSHIMURA Akinori
- Aerospace Research and Development Directorate, Japan Aerospace Exploration Agency (JAXA)
-
- NOJI Yohei
- Department of Mechanical Engineering, Graduate School of Science and Technology, Tokyo University of Science
-
- OGASAWARA Toshio
- Aerospace Research and Development Directorate, Japan Aerospace Exploration Agency (JAXA)
-
- YOKOZEKI Tomohiro
- Department of Aeronautics and Astronautics, School of Engineering, the University of Tokyo
-
- OGIHARA Shinji
- Department of Mechanical Engineering, Faculty of Science and Technology, Tokyo University of Science
Bibliographic Information
- Other Title
-
- 極低温環境下におけるCFRP接着接合のモードII破壊靭性
- キョクテイオン カンキョウ カ ニ オケル CFRP セッチャク セツゴウ ノ モード 2 ハカイジンセイ
Search this article
Abstract
In the present paper, end notched flexure (ENF) tests are conducted for CFRP/CFRP, CFRP/aluminum sheet adhesive bonded specimens at room temperature (296 K), at low temperature (223 K) and at cryogenic temperature (77 K) in order to investigate the mode II adhesive fracture toughnesses. Large difference of the coefficients of thermal expansion (CTE) between the CFRP and the aluminum sheet derives considerable thermal stress at the cryogenic temperature. Therefore, in the ENF tests, the effect of thermal stress must be considered. In the present paper, first the effect of thermal deformation is analytically discussed, and ENF tests are then carried out. The test results reveal that the fracture toughness is much higher at the low temperature than at the room temperature. However, the toughness is significantly lower at the cryogenic temperature than at the low temperature. Moreover, the results show that the crack extends in the adhesive film (cohesive failure) at the room and the low temperatures, whereas it extends at the interface between adhesive film and CFRP (adhesive failure) at the cryogenic. These results imply that the transition of the crack surface caused the degraded adhesive fracture toughness.
Journal
-
- Journal of the Japan Society for Composite Materials
-
Journal of the Japan Society for Composite Materials 37 (4), 130-137, 2011
The Japan Society for Composite Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390001204622515456
-
- NII Article ID
- 10029880849
-
- NII Book ID
- AN00196748
-
- COI
- 1:CAS:528:DC%2BC3MXhtlWqtbbL
-
- ISSN
- 18848559
- 03852563
-
- NDL BIB ID
- 11189300
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed