樹脂埋めしたＣＦ単繊維の圧縮強度

DOI Web Site 被引用文献3件 参考文献38件

書誌事項

タイトル別名
  • Compressive Strength of a Carbon Fiber in Matrix
  • ジュシ ウメ シタ CFタンセンイ ノ アッシュク キョウド

この論文をさがす

抄録

Micro-buckling characteristic of a carbon mono-fiber in matrix was studied. A fiber was modeled in matrix as a column on elastic foundation. Buckling stress of the fiber was calculated incorporating the initial fiber misalignment and non-linearity of the matrix. The effect of bending on compressive stress was also taken into considered to estimate failure initiation at fiber surface. Two processes of ultimate fiber failure were considered. First one is a compressive fracture at fiber surface due to compression and bending. Second one is a matrix-yielding initiated unstable fiber deformation. Compression test of a carbon fiber in matrix was performed by means of a four point bending test. Electrical resistance of the carbon fiber was measured during the compression test to recognize initiation of the compressive fracture. Fiber breaks at two adjacent locations were observed, which was caused by micro-buckling of the fiber. Apparent compressive strength of the fiber was measured in the experiment. Actual compressive strength of the fiber was predicted from the apparent compressive strength. Correlation between compressive strengths based on the elastic foundation model and the kink band model was discussed.

収録刊行物

被引用文献 (3)*注記

もっと見る

参考文献 (38)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ