A New Procedure of the Tensile Fatigue Test for Dental Materials
-
- NISHIMURA Fumio
- Department of Dental Technology I, Faculty of Dentistry, Tokyo Medical and Dental University
-
- NAKAMURA Hideo
- Department of Dental Technology I, Faculty of Dentistry, Tokyo Medical and Dental University
-
- WATARI Fumio
- Department of Dental Technology I, Faculty of Dentistry, Tokyo Medical and Dental University
-
- TANAKA Itaru
- Department of Dental Technology I, Faculty of Dentistry, Tokyo Medical and Dental University
-
- TAKAHASHI Hidekazu
- Department of Fixed Prosthodontics, School of Dentistry, Showa University
Bibliographic Information
- Other Title
-
- 歯科材料引張疲労試験の新しい方法
Search this article
Abstract
A new tensile fatigue test using a stainless steel screw was introduced. A transparent PMMA rod was selected as the test material. A hole was drilled and tapped into the rod; a screw was put into the rod with dental cement or without cementation. Three types of cyclic loads were applied to the test piece; the number of times the load was applied when the initial crack was observed and when the final fracture occurred were recorded. Surface observation showed that actual fatigue fractures occurred in the test piece. The preferred applied load waveform was the cyclic haver-triangles load because of the small coefficient of variance. Fatigue strengths of test pieces with and without cementation were different. Cementation improved the fatigue properties, and the type of cement had an effect on the fatigue properties. Although the number of final fractures minus the number of initial cracks was the constant regardless of the type of cement used.
Journal
-
- Dental Materials Journal
-
Dental Materials Journal 11 (2), 141-149,217, 1992
The Japanese Society for Dental Materials and Devices
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001204717886080
-
- NII Article ID
- 110002983467
-
- NII Book ID
- AA10443149
-
- ISSN
- 18811361
- 02874547
- http://id.crossref.org/issn/02874547
- http://id.crossref.org/issn/01095641
-
- PubMed
- 1304970
-
- Text Lang
- en
-
- Data Source
-
- JaLC
- Crossref
- PubMed
- NDL-Digital
- CiNii Articles
-
- Abstract License Flag
- Disallowed