- LEE Hae-Woo
- Samsung Heavy Industries Co. Welding Research Team, Korea
-
- KANG Sung-Won
- Research Institute of Mechanical Technology, Pusan National Univ., Korea
書誌事項
- タイトル別名
-
- Study on Transverse Weld Cracks in 50mm
この論文をさがす
抄録
This paper was studied in order to clarify the form and position of transverse crack under actual construction condition with SAW (Submerged Arc Welding) process.<BR>In recent years many of the new steel, such as TMCP (Thermo-Mechanical Controlled Process) steel, developments have been intended to improve weldability. TMCP steel have been used achieve high strength with lean compositions, the weld metal is more likely to suffer hydrogen cracking than the HAZ of the parent steel.<BR>Weld metal hydrogen cracking is even more likely if alloying is necessary to match the strength and toughness of the parent metal. This is primarily due to the increased susceptibility to hydrogen cracking of more highly alloyed weld metal.<BR>But most of the published literature on transverse cracks, so far, different compared to the appearance of transverse crack in actual construction.<BR>The reason is a large restraint stress under actual construction compared to a small test piece.
収録刊行物
-
- 溶接学会論文集
-
溶接学会論文集 15 (4), 563-573, 1997
一般社団法人 溶接学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204723352192
-
- NII論文ID
- 130003934470
- 110003421829
-
- NII書誌ID
- AN1005067X
-
- ISSN
- 24348252
- 02884771
-
- NDL書誌ID
- 4354440
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可