周期的マイクロネッキングを持つポリエステル単繊維

DOI 機関リポジトリ HANDLE Web Site Web Site 被引用文献4件 参考文献17件

書誌事項

タイトル別名
  • Periodic Micro-necking of Polyester Filament
  • シュウキテキ マイクロネッキング オ モツ ポリエステル タンセンイ

この論文をさがす

抄録

Periodic necking of micrometer order were generated in polyethylene terephthalate filaments by the crazing method which used tensile stress together with bending stress. PET filament passed to a bending point at a sharp blade (processing edge) under the constant tension. Cycles of the stress concentration and the relaxation were occurred at a pointed end of the processing edge, automatically. The morphology of periodic necking areas depended on the processing angle of bend at the point of the processing edge and the processing stress. Necked PET filament consisted of the necking length of 39-72 μm and the standard deviation of 2.8-6.9 μm for the processing stress of 27-32 MPa and the processing angle of 120 deg. Ratio of generated necking length per non-necking length was 0.2-1.8 (Processing angle: 136 deg.). Although PET filaments of the draw ratio 1.0 and 2.5 formed the periodic necking, those of the draw ratio 4.8 were drawn without the periodic necking. Almost conventional functional fibers were characteristic fibers in a cross sectional shape except thick and thin yarn, however, these periodic micro-necking PET fibers have specific shape in a fiber axis direction.

収録刊行物

  • 繊維学会誌

    繊維学会誌 63 (7), 172-176, 2007

    社団法人 繊維学会

被引用文献 (4)*注記

もっと見る

参考文献 (17)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ