ポリパラフェニレンテレフタルアミド繊維に発現する極限構造について

DOI Web Site 被引用文献1件

書誌事項

タイトル別名
  • CONSIDERATION ON THE RELATION BETWEEN FINE STRUCTURE AND MECHANICAL PROPERTY OF POLY (P-PHENYLENE TEREPHTHALAMIDE) FIBERS

抄録

Previously, it was concluded that poly(p-phenylene terephthalamide) (PPT) fibers comprises a number of pillar-shaped micro-fibrills consisting of extended molecular chains. One of the basis for this notion was the fact that the birefringence calculated for the perfectly uniaxial orientation was less, or at least not greater, than the observed for real PPT fibers. In order to clarify this point, the effect from the interference fringe was taken into account and referred to the result of the electron diffraction measurement. The relation between the fine structure and the mechanical properties of PPT fibers was also studied in the light of the S-S hysteresis behavior, the elongation of fiber period and the structural deformations.<br>The following results were obtained:<br>(1) Assuming that the orientation of the b-axes of crystals of a PPT is radial in the sheath and random in the core, the calculated and observed birefringence became agreeable.<br>(2) The high tenacity and the high modulus of PPT fibers are considered due to the extended chain structure.<br>(3) The remarkable tendency of fibrillization on structural deformation of this fiber, not seen for other synthetic fibers, is also considered to relate to the pillar-shaped micro-fibrill structure. This may lead to poorer fatigue resistance compared with other synthetic fibers, when used as a reinforcement material in rubber.

収録刊行物

  • 繊維学会誌

    繊維学会誌 32 (2), T55-T61, 1976

    社団法人 繊維学会

被引用文献 (1)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ