- THERMAL DEGRADATION BEHAVIORS OF NYLON 4, MODIFIED NYLON 4, AND A COPOLYMER CONTAINING NYLON 4
抄録
Thermal degradation behaviors of nylon 4 homopolymer, a polymer which the chain end of nylon 4 was modified with diamine, and a copolymer containing nylon 4 were investigated by thermal gravimetric analysis at various heating rates. The copolymer (content of nylon 4, 23.5 mole-%) was prepared by anionic copolymerization of α-pyrrolidone and ε-caprolactam.<br>Nylon 4 became more decomposable with a process of degradation reaction. The activation energy of thermal degradation of the polymer was 28-31 kcal/mole, which was smaller than that of nylon 6. The activation energy in the initial stage of degradation depends on the temperature at which degradation of the polymers starts.<br>Thermal stability of the nylon 4 which chain end was modified with bis (p-aminocyclohexyl)-methane increased with rising the temperature of treatment, but its molecular weight remarkably decreased.<br>Thermal stability of the copolymer was considerably superior to that of nylon 4, and in contrast with nylon 4 the copolymer became more non-decomposable with a process of degradation reaction. The degradation reaction proceeded even over the range of nylon 4 contained in the copolymer, indicating occurrence of the degradation reaction of nylon 6 in the main chain of the copolymer.
収録刊行物
-
- 繊維学会誌
-
繊維学会誌 41 (8), T315-T322, 1985
社団法人 繊維学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204863895808
-
- NII論文ID
- 130004074629
-
- ISSN
- 18842259
- 00379875
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可