- PHOTO-INDUCED GRAFT POLYMERIZATION OF METHYL METHACRYLATE ONTO 2, 3-DICARBOXY CELLULOSE
- ヒカリ ショウシャホウ ニヨル 2 3 ジカルボキシ セルロース ノ メタクリ
この論文をさがす
抄録
The photo-induced graft polymerization of methyl methacrylate onto 2, 3-dicarboxy cellulose was carried out in aqueous systems using a quartz and a pyrex tube. The total conversion and the degree of grafting increase with an increase of the carboxyl group content in the cellulose, and reached a levelling-off value at approximately 10 mmol carboxyl group. Grafting efficiency was 90-95%. When the cellulose was treated with sodium borohydride, the degree of grafting and the apparent numbers of grafted chains decreased. The degree of grafting and the molecular weight of grafted chains increased with increasing monomer concentration. The apparent activation energy of graft polymerization onto the celluloses with the carboxyl group contents of 6.8, 18.1 and 55.0 mmol/100g sample were 11.4, 7.3 and 1.1 kcal/mol, respectively.<br>From these results, it is considered that the graft polymerization proceeds mainly via the photolysis of carboxyl groups in the cellulose by the light with the wavelength above 300 nm. On irradiation with the light with the wave length above 253 nm, however, grafting onto the end group, due to the chain scission of the cellulose molecules, concurrently occurred. Termination proceeded by the coupling between the growing polymer radical and cellulose radical, and was accelerated by raising the temperature of the reaction and by irradiation with the light of 253 nm.
収録刊行物
-
- 繊維学会誌
-
繊維学会誌 36 (9), T397-T402, 1980
社団法人 繊維学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001204864052224
-
- NII論文ID
- 130004203408
-
- NII書誌ID
- AN00131651
-
- ISSN
- 18842259
- 00379875
-
- NDL書誌ID
- 2192331
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可