エチレンービニルアルコール共重合体の微細構造と粘弾性的性質

DOI Web Site

書誌事項

タイトル別名
  • THE MICROSTRUCTURE AND THE VISCOELASTIC PROPERTIES OF ETHYLENE-VINYL ALCOHOL COPOLYMERS

抄録

In the previous paper, it was pointed out that in some EVA (Ethylene-vinyl alcohol copolymers) specimen, especially 36.6 mole % vinyl alcohol EVA had a higher ethylene content in the crystalline region rather than that of over-all region.<br>In this paper, in order to clear the relationship between the mechanical properties and the microstructures of EVA, the stress-strain and stress-relaxation behaviour and the dynamic mechanical properties were studied.<br>The following results were obtained: (1) The glass transition temperature and the loss modulus (E″) main peak's temperature of EVA sample which contained 36.6 mole % VA, were higher than those assumed from the copolymer's given composition. (2) The apparent activation energy of mechanical relaxation of the sample mentioned in (1) was 10_??_20 kcal/mole higher than that observed in other copolymers having almost the same over-all copolymer composition. (3) The VA component in the amorphous region and the crystal perfectness affected to the modulus in the leather region.<br>From these results, it may be conclude that even if the over-all copolymer composition of EVA samples are almost same, their mechanical properties are different from each other because of the difference in the VA content and the microstructure of both crystalline and amorphous regions.

収録刊行物

  • 繊維学会誌

    繊維学会誌 33 (2), T49-T55, 1977

    社団法人 繊維学会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ