超微細結晶型鉄基希土類Ｆｅ３Ｂ‐Ｎｄ磁石の高保磁力化

DOI 被引用文献10件 参考文献2件

書誌事項

タイトル別名
  • Improvements in the Coercivity of Iron-Based Nanocrystalline Low-Rare-Earth Fe3B-Nd Permanent Magnets.

抄録

Fe3B-based Nd-Fe-B permanent magnetic materials containing Co and Mas additives, where M is one of Al, Si, Cu, Ga, Ag, and Au, were prepared in an extremely low-rare-earth concentration range of around 4 atomic percent. The hard magnetic properties develop as a result of a heat treatment of rapidly solidified amorphous ribbons, which produces a metastable nanocrystalline structure consisting of Fe3B and Nd2Fe14B. Use of the additives considerably reduces the crystallite sizes, and consequently, the alloys attain higher coercivity than that obtained in alloys without the additives. Compaction-molded resin-borlded magnets produced from the Nd-Fe-B-Co-M materials have the following magnetic propertise: HcJ=300kA/m-470kA/m, Br=0.7 T-0.9 T, and (BH) max=50 kJ/m3-73 kJ/m3. The typical values of the temperature coefficients of Br and HcJ of the bonded magnets are -0.05%/K and -0.35%/K, respectively, in the 297 K-413 K range.

収録刊行物

被引用文献 (10)*注記

もっと見る

参考文献 (2)*注記

もっと見る

キーワード

詳細情報 詳細情報について

  • CRID
    1390001205088074880
  • NII論文ID
    130004924242
  • DOI
    10.3379/jmsjmag.17.185
  • COI
    1:CAS:528:DyaK2MXis1Gktro%3D
  • ISSN
    18804004
    02850192
    http://id.crossref.org/issn/02850192
  • 本文言語コード
    ja
  • データソース種別
    • JaLC
    • Crossref
    • CiNii Articles
  • 抄録ライセンスフラグ
    使用不可

問題の指摘

ページトップへ