Some Properties of Co-Ni-Mn Spinel Ferrite Fine Particles Prepared by the Chemical Coprecipitation Method with Various Preparation Conditions

DOI NDL Digital Collections Web Site 1 Citations 16 References

Bibliographic Information

Other Title
  • 化学的共沈法によるＣｏ‐Ｎｉ‐Ｍｎスピネル系微粒子の作製条件による諸特性
  • 化学的共沈法によるCo-Ni-Mnスピネル系微粒子の作製条件による諸特性
  • カガクテキ キョウチンホウ ニ ヨル Co Ni Mn スピネルケイ ビリュウシ ノ サクセイ ジョウケン ニ ヨル ショトクセイ

Search this article

Description

An experiment was carried out to investigate the effect of MnO substitution, mole ratio n { = Fe3+/(Co2++Ni2++Mn2+)}, reaction temperature, and concentration of alkali on the magnetic and physical properties of Co-Ni-Mn ferrite prepared by the chemical coprecipitation method without post-annealing. The chemical coprecipitation compositions were chosen according to the formula (CoO)0.5(NiO)0.5-x(MnO)x·n/2(Fe2O3), where x varied between 0 and 0.5 and n varied between 1.80 and 2.00. To remove the superparamagnetic substance, the coprecipitation fine particles were etched with dilute sulfuric acid. As a result, in the (CoO)0.5(NiO)0.3(MnO)0.2·1.95/2(Fe2O3) composition, when the reaction temperature and excess NaOH were 60°C and 0.5 mol, the following magnetic and physical properties were obtained: saturation magnetization σs = 79.77×10-6 Wb·m/kg, residual magnetization σr = 47.38×10-6 Wb·m/kg, coercivity HcJ = 184 kA/m, and average particle size D = 19.61 nm.

Journal

Citations (1)*help

See more

References(16)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top