Improvement of Formability in Cold Rolling of Hot Band for Over 980 MPa Grade High Tensile Strength Steel Sheet

DOI Web Site Web Site 3 References

Bibliographic Information

Other Title
  • 冷延980MPa超級ハイテン用熱延鋼板の冷間圧延特性改善
  • レイエン 980MPa チョウキュウ ハイテンヨウ ネツエン コウバン ノ レイカン アツエン トクセイ カイゼン

Search this article

Description

To produce high tensile strength steel sheets in cold rolling with good thickness accuracy, it is important to supply material hot bands without harmful fluctuations in their deformation resistance. For the purpose, it is effective to set a high coiling temperature in the hot rolling stage.<br/>On the other hand, it is well known that the surfaces of steel sheets easily form oxide at a high temperature in the case of steel grade which contains Si and Mn in its chemical composition. To avoid the formation of oxide, it is necessary to set a low coiling temperature in the hot rolling stage.<br/>By the conventional hot rolling conditions, it is difficult to satisfy conditions both to get uniform formability in cold rolling and to prevent the surface of hot strips from forming internal oxidation zone.<br/>This report describes the improvement on the mechanical property without harmful internal oxidation zone of hot strips by the proper heat histories in manufacturing the hot rolled 0.17C-1.3Si-2.0Mn high tensile steel sheet.

Journal

  • Tetsu-to-Hagane

    Tetsu-to-Hagane 100 (5), 616-624, 2014

    The Iron and Steel Institute of Japan

References(3)*help

See more

Keywords

Details 詳細情報について

Report a problem

Back to top