耐熱合金Timken 16-25-6に関する研究(III)

DOI Web Site 被引用文献1件

書誌事項

タイトル別名
  • STUDY ON TIMKEN 16-25-6 TYPE HEAT-RESISTING ALLOY (III)
  • 焼戻における諸変化および析出物について
  • Change of the Properties during Tempering and Precipitates

この論文をさがす

説明

Change of the properties during tempering (0°-1000°C) of the solution-treated (1250°C×1h. W.C.) Timken 16-25-6 alloy were studied by measuremnt of hardness, differential dilatation, specific heat, electric resistance and microstructure.<BR>By electron microstructural studies, X ray diffraction analysis and chemical analysis of electrolytically separated residues, the microconstituents of the aged (550°-900°C) Timken 16-25-6 alloy were studied.<BR>The results were summerized as follows:<BR>(1) Two Stages of contraction, heat evolution and decrease of electric resistance at 500°-550°C and 750°C-1000°C by the precipitation were observed during tempering of the solution-treated Timken alloy. The tbmperature range and the amount of changes of the latter was greater than that of the former. It seemed that at least there were two kinds of precipitates at 700°-1000°C and the transition temperature of these was at about 825°C.<BR>(2) From the dilatation change, it seemed that the precipitate below 600°C dissolved once, and at above 700°C another precipitation occured, but the precipitate above 800°C existed with the precipitate below 800°C.<BR>(3) The microconstituents of Timken 16-25-6 alloy were composed of double carbide M4C; {(Cr, Fe, Ni)3Mo1}C below 800°C and double nitride CrMoNx; {(Cr, Fe, Ni)1Mo1}N1 as well as double carbide M6C; {Cr, Fe, Ni)5Mo1} C above 800°C.<BR>No evidence was found of the formation of sigma phase in this alloy.

収録刊行物

  • 鉄と鋼

    鉄と鋼 42 (12), 1132-1138, 1956

    一般社団法人 日本鉄鋼協会

被引用文献 (1)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ