固体ＣａＯ‐溶融スラグ界面におけるＰ２Ｏ５含有相の微視的生成機構

DOI Web Site Web Site 被引用文献17件 参考文献25件
  • 齊藤 礼太
    東京大学大学院新領域創成科学研究科物質系専攻
  • 松浦 宏行
    東京大学大学院新領域創成科学研究科物質系専攻
  • 中瀬 憲治
    東京大学大学院新領域創成科学研究科物質系専攻
  • 楊 肖
    東京大学大学院新領域創成科学研究科物質系専攻
  • 月橋 文孝
    東京大学大学院新領域創成科学研究科物質系専攻

書誌事項

タイトル別名
  • Microscopic Formation Mechanisms of P2O5-containing Phase at the Interface between Solid CaO and Molten Slag
  • 固体CaO-溶融スラグ界面におけるP2O5含有相の微視的生成機構
  • コタイ CaO ヨウユウ スラグ カイメン ニ オケル P2O5 ガンユウソウ ノ ビシテキ セイセイ キコウ

この論文をさがす

説明

It is quite important to reveal the microscopic reaction mechanisms and the role of the solid and liquid phases in the solid CaO coexisting flux in the hot metal dephosphorization process. In the present study, solid CaO piece and FeOx–CaO–SiO2–P2O5 slag with various FeOx and P2O5 contents, and CaO/SiO2 ratios of the slag were reacted at 1573 and 1673K. The interface between solid CaO and molten slag was observed and analyzed by SEM/EDS. Microscopic reaction mechanisms between solid CaO and molten slag was discussed with changing reaction times, slag compositions and temperatures. The CaO–FeOx phase adjacent to solid CaO, and the CaO–SiO2 or CaO–SiO2–P2O5 solid phase coexisting with the FeOx–CaO–SiO2 liquid slag next to the CaO–FeOx phase were observed for all slag compositions, temperatures and reaction times. Phosphorus was condensed as 2CaO·SiO2–3CaO·P2O5 phase more easily in the case of higher CaO/SiO2 ratio and higher FeOx content in slag. There was a linear relationship between P2O5 content in 2CaO·SiO2–3CaO·P2O5 phase and the distance from CaO–FeOx phase to 2CaO·SiO2–3CaO·P2O5 phase. The P2O5 content increased from CaO–FeOx boundary toward bulk slag, and P2O5 content in the condensed phase near the CaO–FeOx phase increased with increasing reaction time. This P2O5 concentration gradient tended to diminish. These results suggest that the condensation of phosphorus as 2CaO·SiO2–3CaO·P2O5 phase was controlled by P2O5 diffusion from bulk slag to reaction interface, not by absorption of P2O5 into 2CaO·SiO2 particle.

収録刊行物

  • 鉄と鋼

    鉄と鋼 95 (3), 258-267, 2009

    一般社団法人 日本鉄鋼協会

被引用文献 (17)*注記

もっと見る

参考文献 (25)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ