書誌事項
- タイトル別名
-
- In-situ Observation of Ferrite Plate Formation in Low Carbon Steel during Continuous Cooling Process
- テイタンソコウ ノ レンゾク レイキャク カテイ ニ オケル フェライト プレート ケイセイ ソノバ カンサツ
この論文をさがす
抄録
In-situ observation of austenite-to-ferrite transformation in low carbon steel was conducted with a laser scanning confocal microscope. Development and kinetics of ferrite plates during continuous cooling process were studied. It was in-situ observed that the ferrite plates nucleated at either austenite grain boundary or allotriomorphic ferrite, and grew with keeping the Kurdjumov–Sachs orientation relationship with prior austenite. Surface relief was induced by the formation of ferrite plate. When the ferrite plate nucleated at pre-existing grain boundary ferrite, gradual change in growth direction by the sympathetic nucleation was confirmed both by the observation and EBSP analysis. Temperature dependency of the observed growth rates of the plates was in a good agreement with the Zener–Hillert model, which indicates the growth is controlled by the diffusion of carbon.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 94 (9), 363-368, 2008
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205128379136
-
- NII論文ID
- 110006894485
-
- NII書誌ID
- AN10528571
-
- ISSN
- 1341688X
- 18832954
- 00211575
-
- NDL書誌ID
- 9636276
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可