脱酸剤の静止溶鉄中への溶解と移動現象

DOI Web Site Web Site 被引用文献1件 参考文献1件

書誌事項

タイトル別名
  • Dissolution and Transport Phenomena of Deoxidizing Elements into Quiescent Molten Iron
  • ダッサンザイ ノ セイシ ヨウテツチュウ エ ノ ヨウカイ ト イドウ ゲンシ

この論文をさがす

抄録

This work was carried out to obtain the knowledge of dissolution and the transport phenomena of deoxidizing elements into quiescent liquid iron.<BR>Deoxidizers were added as block state or as liquid state on the surface of liquid iron melted in a tammann furnace. Changes of the temperature near the surface of the liquid iron were measured with thermocouples. After a predetermined holding time in the furnace, each heat was rapidly quenched into water. Concentration contours of deoxidizing elements were obtained on the surface by XMA point analyses. The results obtained are summarised as follows.<BR>(1) When deoxidizer was added as liquid state, the deoxidizing elements were transferred into liquid iron by diffusion. The diffusion co-efficient of aluminum in liquid iron was obtained as 1.12×10-4 cm2/sec.<BR>(2) When deoxidizer was added as block state, the temperature near the surface went down. Owing to this temperature-drop, convection in the liquid iron occurred and deoxidizing elements were transferred with convection. This convection in the case of solid aluminum with dense and tight oxide film was stronger than that of silicon without a tight oxide film.<BR>(3) When aluminum was transferred with convection, it produced high concentration regions. These regions floated up without reaction and diffusion. Owing to this phenomena, the yield of aluminum was scattered.

収録刊行物

  • 鉄と鋼

    鉄と鋼 64 (14), 2119-2128, 1978

    一般社団法人 日本鉄鋼協会

被引用文献 (1)*注記

もっと見る

参考文献 (1)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ