- Design of Titanium Alloys Suitable for Superplastic Forming
- チョウソセイ カコウ ニ テキシタ Ti ゴウキン ノ セッケイ
この論文をさがす
抄録
Using four kinds of α+β titanium alloys (Ti-Al-V-Sn-Zr-Mo-Cr-Fe system), the effects of test temperature and volume fraction of α phase on superplastic properties were investigated.<BR>(1) Total elongation of each alloy was more than 400% in the temperature range between 1023 K and 1123 K at the strain rate of 6.7×10-4 s-1. Maximum flow stress increased with decreasing temperature rapidly in the temperature range lower than 1073 K. From these results, the temperature range between 1073 K and 1123 K was considered to be suitable for superplastic forming of these alloys at the strain rate of 6.7×10-4 s-1.<BR>(2) The effects of test temperature and volume fraction of α phase on the strain rate sensitivity, m, were examined by multiple regression analysis. Following regression equation was obtained.<BR>m=-17.128(Θ-1.095)2-0.514(Vα-0.426)2+0.422<BR>Θ : Test temperature K×10-3, Vα : Volume fraction of α phase<BR>From this equation, titanium alloys whose volume fraction of α phase is 0.426 at the temperature of 1095 K are considered to give the maximum m value and the best superplastic properties at a strain rate of 6.7×10-4 s-1.<BR>(3) α phase was formed at the surface of specimen due to the reaction with oxygen during high temperature tensile test in an argon atmosphere. Such α phase was expected to be detrimental for superplastic forming and to reduce ductility of the material.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 74 (1), 123-129, 1988
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205150895232
-
- NII論文ID
- 110001492127
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 3157776
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可