- Effect of Molybdenum Content on Creep-rupture Strength and Toughness of 9% Chromium Ferritic Heat Resisting Steels Containing V and Nb
- V,Nb添加9%Crフェライト系耐熱鋼のクリープ破断強度と靭性におよぼすMo量の影響
- V Nb テンカ 9パーセント Cr フェライトケイ タイネツ コウ ノ クリ
この論文をさがす
抄録
The effect of molybdenum content on creep-rupture properties and room-temperature toughness of high chromium ferritic heat resisting steels was investigated. Molybdenum content was varied from 1 to 2 wt%. In order to obtain 9Cr-Mo-V-Nb ferritic steels with both high creep-rupture strength and superior toughness, the amount of delta ferrite was controlled below 25%, and the optimum tempering condition and mechanical properties after simulated welding have been investigated. The influence of molybdenum content on creep-rupture strength and Charpy absorbed energy was investigated with respect to the ratio of delta ferrite to tempered martensite, the precipitates, and the microstructures.<BR>Charpy absorbed energy of the 0.05C-9Cr-1Mo-0.15V-0.05Nb steel tempered at 800°C and then heated at 600 650°C for 104 h was as high as 20 30 kgf-m. By contrast, Charpy absorbed energy of 0.05C-9Cr-2Mo-0.15V-0.05Nb steel was reduced to about 4 kgf-m after heating at 600 650°C for 104 h. It is considered that the steel of 1Mo shows superior toughness because of its low carbon content and a single phase of martensite. It was concluded that combination of superior creep-rupture strength and toughness can be obtained by optimum heat treatment for the 9Cr-1Mo-V-Nb steel containing 0.05 wt%C.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 74 (10), 2001-2008, 1988
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205150941696
-
- NII論文ID
- 110001492159
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 3196577
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可