書誌事項
- タイトル別名
-
- Superplastic Behaviour and Optimum Work Processing of a Powderconsolidated and Extruded Ni-base Superalloy
- ショウケツ Niキ チョウ タイネツ ゴウキンフンマツ オシダシザイ ノ チョ
この論文をさがす
抄録
The powder of nickel-base suneralloy Mod. IN-100 was consolidated by hot isostatic pressing and recrystallized under the conditions of extrusion ratio of 72% at 1 373 K and subsequent annealing at 1 343 K×1h. The fine grain size of 1.5 μm in diameter was obtained.<BR>The superplastic behaviour of alloy bars mentioned above was investigated in the temperature range of 1 2231 423 K and in the range of strain rates from 2.5 × 10-4 to 10-1 s-1.<BR>The ln σ vs. ln ε curves were obtained. It was shown that the conditions obtaining the maximum strainrate sensitivity index, m changed from the constant strain rate of 10-2 s-1 at temperatures above 1 303 K to the constant flow stress of 150 MPa below 1 303 K. Therefore, it was possible to divide the ln σ vs. ln ε curves into six regions according to the deformation behaviour.<BR>Furthermore, it was desirable to decrease the temperature continuously for the purpose of keeping the maximum m during superplastic deformation in tensile test. In fact, the total elongation exceeded extremely as compared with the isothermal test.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 74 (1), 115-122, 1988
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205151003904
-
- NII論文ID
- 110001492126
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 3157867
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可