最終コークス温度600-900℃に乾留されたコークスの性状

岩切 治久

doi:10.2355/tetsutohagane1955.78.8_1314

書誌事項

タイトル別名

Properties of Coke Carbonized at 600-900°C Final Coke Temperature
サイシュウコークスオンド 600 900ドC ニカンリュウサレタコーク
Properties of Coke Carbonized at 600-900°C Final Coke Temperature

この論文をさがす

説明

Properties of coke which was carbonized at lower temperatures than in the conventional process were examined experimentally, and the possibility of its use in a blast furnace was discussed. The following results were obtained: (1) When coke was carbonized under the conditions of final coke temperature higher than 800°C and higher heating rate, the same level of coke strength as that of conventional coke was obtained. (2) The heating rate in the coal bed between 400°C and 500°C and the bulk density of charged coal controlled the pore structure, and were also important factors in determining coke qualities. (3) It was noticed that the coke qualities might be improved by heat treatment in a blast furnace before the occurrence of coke degradation by solution-loss reaction. (4) In order to obtain a higher heating rate in the coal bed, it was required that the chamber wall was constructed by the materials with high thermal-conductivity or that the thickness of chamber wall became thinner.

収録刊行物

鉄と鋼

鉄と鋼 78 (8), 1314-1321, 1992

一般社団法人日本鉄鋼協会

キーワード

詳細情報詳細情報について

書き出し

問題の指摘