オーステナイトステンレス鋼の分極下での水素脆化挙動と応力腐食割れの関連性について

DOI Web Site Web Site 参考文献22件

書誌事項

タイトル別名
  • Relation between Hydrogen Embrittlement Behavior and Stress Corrosion Cracking of Austenitic Stainless Steel under Anodic and Cathodic Polarization
  • オーステナイトステンレス コウ ノ ブンキョク カ デ ノ スイソゼイカ キョドウ ト オウリョク フショク ワレ ノ カンレンセイ ニ ツイテ

この論文をさがす

説明

In order to study the behavior of hydrogen embrittlement under anodic and cathodic polarization of austenitic stainless steels, were measured the change in ductility and amount of adsorbed hydrogenin the 18Cr-8Ni and 25Cr-20Ni stainless steels in H2SO4, HCl, NaCl and MgCl2 solutions.<BR>The main results obtained are as follows:<BR>(1) Hydrogen absorption and embrittlement occurs in chloride solution under anodic polarizationbut not in H2SO4 solution.<BR>(2) This hydrogen adsorption was closely connected with the operation of local corrosion cell sassociated with pits on the surface of the steel.<BR>(3) It is significant that the pitting and the associated hydrogen adsorption in these steels play animportant role for stress corrosion cracking. Therefore impressed anodic current can reduce the stresscorrosion cracking time.

収録刊行物

  • 鉄と鋼

    鉄と鋼 56 (6), 784-795, 1970

    一般社団法人 日本鉄鋼協会

参考文献 (22)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ