高Mn-Cr-Ni鋼の組織, 透磁率および電気抵抗について

DOI Web Site Web Site

書誌事項

タイトル別名
  • Microstructure, Magnetic Permeabiiity and Electric Resistivity of High Manganese-Chromium-Nickel Steel
  • コウ Mn Cr Ni コウ ノ ソシキ トウジリツ オヨビ デンキ テイコウ

この論文をさがす

抄録

In order to investigate the austenitic steel with the non-magnetic characteristics, microstructures, mechanical properties, magnetic permeability and electric resistivity of manganese-chromium-nickel steels with much amount of manganese as an austenitizing element have been examined. The results obtained are as follows.<BR>It was found that composition range showing stable austenite phase lays on the higher content side of the line connecting approximately 10Mn-10Cr and 20Mn-0Cr in Mn-Cr-1%Ni phase diagram. This composition range moved to the line connecting approximately 20Mn-10Cr and 23Mn-0Cr in the case of cold rolled steel plate. High toughness and magnetic permeability (μ) under 1.01-1.02 were obtained in the steel with complete austenite phase. Magnetic permeability markedly increased by small amount of martensite in austenite phase. Therefore, it is necessary that nonmagnetic steel have complete austenite phase. The relationship between electric resistivity (ρ) and alloying element; manganese, chromium, nickel, silicon in austenite phase, can be written as ρ=1.27 [%Mn] +0.66 [%Cr] +1.62 [%Ni] +5.90 [%Si] +36 (μΩ-cm). From the above results, 25Mn-5Cr-1Ni steel may be selected as an optimum composition from the view points of stable austenite, high toughness, non-magnetism and suitable electric resistivity.

収録刊行物

  • 鉄と鋼

    鉄と鋼 65 (9), 1434-1439, 1979

    一般社団法人 日本鉄鋼協会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ