還元鉄ペレットの溶鉄中への溶解速度におよぼす溶澤の影響

DOI Web Site Web Site

書誌事項

タイトル別名
  • Effect of Molten Slag on the Dissolving Rate of Reduced Iron Pellets into Iron Melt
  • 還元鉄ペレットの溶鉄中への溶解速度におよぼす溶滓の影響
  • カンゲン テツ ペレット ノ ヨウテツチュウ エ ノ ヨウカイ ソクド ニ オ

この論文をさがす

抄録

The effect of molten slag on iron melt upon the dissolving rate of cylindrical reduced iron pellets made from Höganäs iron powders, Fe2O3 powders and pulverized additives was investigated. The following results were obtained:<BR>(1) A small portion of iron oxide in pellets dissolved into the molten slag. The dissolving rate of pellets into iron melt was determined by neglecting the reduction of iron oxide in molten slag.<BR>(2) The maximum dissolving rate appeared at about unit basicity of molten slag. The effect of molten slag on the dissolving rate could be explained from their viscosity and density. The molten slag of the lower viscosity and the lower density would be desirable for higher dissolving rates.<BR>(3) The effect of molten slag with basicity of 0.5 and 1 on the temperature dependence of the dissolving rate into iron melt was small for pellets containing Fe2O3 and large for those without Fe2O3.<BR>(4) The molten slag with unit basicity had little effect on the dissolving rate of pellets containing CaO, CaCO3, C and flux (simultaneous addition of CaO and SiO2). The iron oxide which dissolved into the molten slag increased with increasing prefused slag, SiO2, and Al2O3 contents in pellets.

収録刊行物

  • 鉄と鋼

    鉄と鋼 65 (12), 1683-1691, 1979

    一般社団法人 日本鉄鋼協会

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ