Effects of Aging Conditions and Strain Rate on Rupture Elongation of 13Ni-15Co-10Mo-0.2Ti (280kg/mm<SUP>2</SUP>-Grade) Maraging Steels
-
- SOENO Kô
- Hitachi Research Laboratory, Hitachi Ltd.
-
- TAGUCHI Kazuo
- Hitachi Research Laboratory, Hitachi Ltd.
-
- TUCHIYA Masatoshi
- Hitachi Research Laboratory, Hitachi Ltd.
Bibliographic Information
- Other Title
-
- 13Ni-15Co-10Mo-0.2Ti (280kg/mmmm<SUP>2</SUP>級) 系マルエージ鋼の延性に及ぼす時効条件と歪速度の影響
- 13Ni-15Co-10Mo-0.2Ti(280kg/〓級)系マルエージ鋼の延性に及ぼす時効条件と歪速度の影響
- 13Ni 15Co 10Mo 0 2Ti 280kg キュウ ケイ マルエージ
Search this article
Abstract
Tensile strength and elongation have been measured in aged 13Ni-15Co-10Mo-0.2Ti, 14Ni-10Co-10Mo and 14Ni-15Co-7Mo maraging steels. The temperature range in aging has been varied from 450°C to 575°C for the 13Ni-15Co-10Mo-0.2Ti steel, and from 425°C to 475°C for the 14Ni-10Co-10Mo and 14Ni-15Co-7Mo steels. A cross head speed in a tensile test has been ranged from 1mm/min to 0.005mm/min. The effect of strain rate on tensile elongation has been investigated in relation to aging temperature and time.<BR>In tensile tests of the maraging steels in which fine coherent precipitates are considered to be formed, it is observed that tensile elongation is decreased with decreasing a strain rate. The elongation decrease in a low strain rate is also observed in tensile tests of the 13Ni-15Co-10Mo-0.2Ti steel in which coarse precipitates are contained by over-aging. It is considered that the elongation decrease in a low strain rate is attributed to both stress concentrations resulting from plastic deformation characteristics of the aged maraging steels and hydrogen diffused to regions having intense stress concentrations.
Journal
-
- Tetsu-to-Hagane
-
Tetsu-to-Hagane 65 (6), 665-673, 1979
The Iron and Steel Institute of Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390001205154533888
-
- NII Article ID
- 110001487949
-
- NII Book ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL BIB ID
- 2052114
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed