18-8 Mo-Cb鋼の高温における動クリープおよび疲れ

DOI DOI Web Site Web Site Web Site

書誌事項

タイトル別名
  • Dynamic Creep and Fatigue of a 18-8 Mo-Cb Steel at Elevated Temperature
  • 18-8Mo-Cb コウ ノ コウオン ニ オケル ドウ クリープ オヨビ ツカレ

この論文をさがす

抄録

Dynamic creep and fatigue tests were conducted on a 18-8 Mo-Cb steel at a temperature of 650°C. The results were discussed from the standpoint of the analysis which had been proposed by the authors previously to predict the dynamic creep and the fatigue strength from the static creep and rupture data together with reversed stress fatigue data. The prediction by the analysis showed a quite satisfactory agreement with the experimental results for the practical purpose, although a little discrepancy was observed due to the acceleration of the precipitation hardening by alternating stress. As a contribution to make clear the relation of the precipitation hardening characteristics of the material to its strength characteristics, especially the discrepancy between the analytical and experimental strengths, the following tests were also carried out, (1) the hardeness test of the material before and after the dynamic creep, (2) the observation of structure before and after the dynamic creep by an electron microscope, (3) the creep rupture test after the dynamic creep. According to the results of these tests, the variations of structure and of hardness during the dynamic creep process seemed not to be related directly with the discrepancy, but the results of the creep rupture test after the dynamic creep showed appreciably greater life than in the case of static creep rupture, and it was believed certain that the cause of the discrepancy consisted in strengthening of the material by the alternating stress related to the precipitation hardening.

収録刊行物

詳細情報 詳細情報について

問題の指摘

ページトップへ