Specimens applied to tests were made of the Ziegler type polyethylene rolled and/or irradiated with gamma-ray from cobalt 60 under immersion in water and then were heat-treated in boiling water for one hour to stabilize the polyethylene materials. An Instron tester was employed to measure the yield points of all specimens at the cross-head speeds of 0.5, 3.0 and 20 cm/min at a temperature of 30°C. Concluding remarks are as follows : the yield point of polyethylene increases with increasing cross-hear speed, but the yield point ratio (which is defined as the ratio of yield point of irradiated polyethylene to the yield point of non-irradiated polyethylene) becomes smaller when tensile test is performed at higher speed than it is done at lower speed.
収録刊行物
-
- 日本機械学會論文集
-
日本機械学會論文集 28 (188), 559-564, 1962
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205158595968
-
- NII論文ID
- 110002460586
- 110002356896
-
- NII書誌ID
- AN00187419
-
- ISSN
- 21859485
- 24242675
- 00290270
-
- NDL書誌ID
- 9150944
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可