- Studies on the Surface Layer of Machined Steel : 1st Report, Machined Surface Layer of High Manganese-Chromium Steel and its Influences on Results of Tensile Test
- キカイ シアゲ サレタ コウザイ ノ カコウ ヘンシツソウ ノ ケンキュウ 1
この論文をさがす
抄録
The depth and the degree of work hardening of the surface layers of tensile specimen of high Mu-Cr steel finished under several conditions (turning, grinding, polishing and electro-polishing) were studied experimentally as a function of depth of cut. Then, the behavior of these surface layers under the tensile load test was observed through a microscope. The conclusion of these studies are as follows : (i) The depth of surface layer and the degree of work hardening (we defined tentatively Hw as the representation of this degree) are relative to the depth of cut at finishing condition. (ii) The work hardening to these surface layers affects the local contraction of specimen and under some finishing condition invites the surface cracking. (iii) The notch effect caused by cracking and the stress concentration in the surface layer are the reason for the influences ascribed above.
収録刊行物
-
- 日本機械学會論文集
-
日本機械学會論文集 27 (182), 1620-1627, 1961
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205158929920
-
- NII論文ID
- 110002351517
-
- NII書誌ID
- AN00187419
-
- ISSN
- 21859485
- 00290270
-
- NDL書誌ID
- 9150844
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可