- An Experiment on the Effect of Induction Hardening of Fatigue Strength : Report 3
- コウシュウハ ヤキイレ ノ ツカレ ツヨサ ニ カンスル エイキョウ ニ ツイテ ノ イチ ジッケン 3
この論文をさがす
抄録
The authors have conducted fatigue tests on induction hardened V-notched specimens (ρ=0.25mm, 0.5mm, 1mm and 5mm) with C=0.13% steel. Induction-heating temperature was chosen 700°C, 800°C, 900°C, 1000°C, and 1100°C. The experimental results may be summarized as follows : (i) There is a favourable difference between σw1and σw2, when ρ is 0.25mm, 0.5mm, or 1mm; but no difference between σw1and σw2 at ρ=5mm. (ii) The absolute values of σw2 reach a maximum at 1100°C, and decrease as the heating temperature decrease. The value of σw1 at 1100°C is higher then that at the other temperatures, but the values of σw1 show no difference from those at other temperatures. The values of σw1 andσw2 are almost proportional to the hardness at the notched-bottom, within the range of these experiments. (iii) For discussion of the crack-development, we calculated the stress of crack-tip with simple form, and examined the simple relation between the calculated-stress and hardness.
収録刊行物
-
- 日本機械学會論文集
-
日本機械学會論文集 29 (200), 719-728, 1963
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205159342592
-
- NII論文ID
- 110002351828
-
- NII書誌ID
- AN00187419
-
- ISSN
- 21859485
- 00290270
-
- NDL書誌ID
- 9151151
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可