- On the Abrasion Test of High Manganese Point : Wear of Deposited Weld High Manganese Metal
- コウマンガン テンテツキ ノ マモウ シケン
この論文をさがす
抄録
To find out the prevention of defacement in case of deposited weld high manganese metal used for points of the railway, I have conducted experiments under the following conditions, i.e., lubricated and non-lubricated states and determinations made by using an Amsler type abrasion testing machine, employing slip velocities ranging from 0 to 15 cm/sec and contact pressures between 50 and 90 kg/mm2. The test piece of tyre is about 0.7%C standard structure steel, and the other material of deposited weld high manganese metal. The results of tests indicated that : - 1) "Pitting" amount of the deposited weld high manganese metal is very little, and the effect of lubrication is very remarkable. 2) In case of austenitic structure, deposited weld high manganese metal, shows the same tendency of wear as cast high manganese steel.
収録刊行物
-
- 日本機械学會論文集
-
日本機械学會論文集 28 (194), 1384-1393, 1962
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205159631360
-
- NII論文ID
- 110002351704
- 110002351646
-
- NII書誌ID
- AN00187419
-
- ISSN
- 21859485
- 00290270
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可