- Fatigue Damage of 6-4 Brass Specimens
- クリカエシ オウリョク ニ ヨッテ 6-4 オウドウ ガ ウケル ヒガイ ニ ツイテ
この論文をさがす
抄録
By annealing and electro-polishing technique it was shown that the fatigue damage of 6-4 brass specimens is confined within a thin surface layer of the specimens. The thickness of the damaged layer becomes thicker when the applied stress is high and the number of stress repetitions is large. The rate of growth of the thickness of the damaged layer begins to increase rapidly, when its thickness exceeds some threshold value (in the present case, 30∼50 microns). The fatigue damage occurring beneath the surface layer of the specimen seems to be of strain-hardening character and it disappears by stress relief annealing. It seems from this work that the fatigue limit is the stress under which the thickness of the damaged layer remains within some limit, even if the number of stress repetitions is infinitely large.
収録刊行物
-
- 日本機械学會論文集
-
日本機械学會論文集 28 (194), 1301-1305, 1962
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205159676928
-
- NII論文ID
- 110002351694
- 10009838523
-
- NII書誌ID
- AN00187419
-
- ISSN
- 21859485
- 00290270
-
- NDL書誌ID
- 9151035
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可