- Plastic Anisotropy in an Electrodeposited Pure Iron
- 力学特性 高純度電解析出鉄における塑性異方性
- リキガク トクセイ コウジュンド デンカイ セキシュツテツ ニ オケル ソセイ イホウセイ
この論文をさがす
抄録
Deformation behavior of electrodeposited plates of pure iron was studied. The plate consisting of fine cdamnar grains with (III) fiber texture was found to show Rankford (γ) value as large as 7.6 at 293K. When test temperature was lowered to 77k, the r-value was decreased. The r-value was also decreased when specimens were annealed to enlarge grain size. From observations of surface believes and substructures of deformed specimens, it is speculated that such an extromoly high r-value is mainly caused by grain boundary sliding.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 88 (11), 801-807, 2002
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205181891456
-
- NII論文ID
- 110001457389
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
- http://id.crossref.org/issn/00211575
-
- NDL書誌ID
- 6341597
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可