りん含有フェライト黒鉛鋼の脆性

DOI Web Site Web Site 参考文献9件

書誌事項

タイトル別名
  • The Embrittlement of Ferritic Graphite Steel Containing Phosphorus
  • リン ガンユウ フェライト コクエン コウ ノ ゼイセイ

この論文をさがす

抄録

In order to investigate the embrittlement of blackheart malleable iron, Charpy impact tests are carried out for series of ferritic graphite steel specimens having the same chemical composition as blackheart malleable iron except for carbon content. IMA analysis has also been employed on the grain boundary fracture surface of the embrittled iron.<BR>The results obtained are as follows :<BR>(1) Quenching from 450°C without holding at this temperature shows some degree of embrittlement, i. e. ΔTr+55°C.<BR>(2) Quenching from 450°C after 1 hour holding at this temperature shows remarkable embrittlement, while quenching from 650°C shows some degree of de-embrittlement. Moreover, it has been clarified that the complex combination of embrittling and de-embrittling treatments changes the behaviour of embrittlement in ferritic graphite steel.<BR>(3) Heat treatment at 300°C after embrittling treatment at 450°C shows considerable degree of de-embrittlement.<BR>(4) IMA analysis has detected the remarkable segregation of phosphorus on the grain boundary fracture surface of embrittled specimen.<BR>(5) It is assumed from results obtained that the segregating behaviour of carbon atoms contributes to the embrittling phenomenon of ferritic graphite steel by larger interaction behaviour of phosphorus atoms in grain boundary zone.

収録刊行物

  • 鉄と鋼

    鉄と鋼 68 (3), 506-513, 1982

    一般社団法人 日本鉄鋼協会

参考文献 (9)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ