耐スキャブ腐食性に影響を及ぼすりん酸塩皮膜の構造

DOI Web Site Web Site 参考文献1件 オープンアクセス

書誌事項

タイトル別名
  • The Structure of Phosphate Crystals Influencing the Scab Corrosion Resistance
  • タイ スキャブ フショクセイ ニ エイキョウ オ オヨボス リンサンエン ヒマ

この論文をさがす

説明

The structure of phosphate crystals that exerts a favorable effect on the scab corrosion resistance on the painted steel surface was investigated and characterized by 1) a low Zn/P intensity ratio measured by glow discharge spectrometry, 2) a low preferred orientation of the (100) plane in phosphophyllite, and 3) angular and granular phosphate crystal morphology.<BR>The aforementioned structure of phosphate crystals depends on the crystal growth process. When the dissolution of iron from the steel sheet during the phosphating treatment is insufficient, the hopeite epitaxial growth plane (020) conforms to the phosphophyllite epitaxial growth plane (100), and the mixed crystals with a high Zn/P ratio grow along the steel surface. When the dissolution of iron from the steel sheet is sufficient, the iron ion concentration in the solution increases, the intrinsically free precipitation of phosphophyllite without the restraint of epitaxy becomes predominant, and phosphate crystals with a lower Zn/P ratio grow.<BR>The dissolution of iron from the steel sheet is accelerated by the oxides of manganese and silicon in a surface layer of up to 0.1 μm deep that is dissolved during the phosphating treatment.

収録刊行物

  • 鉄と鋼

    鉄と鋼 77 (7), 1050-1057, 1991

    一般社団法人 日本鉄鋼協会

参考文献 (1)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ