書誌事項
- タイトル別名
-
- The Compound Dependent Intergranular Corrosion Mechanism in Stainless Steels
- ステンレス コウ ニ オケル カゴウブツ イゾンガタ リュウカイ フショク キ
この論文をさがす
抄録
Following the first paper on the study of the composition dependent intergranular corrosion (IGC) mechanism of stainless steels (SS), the compound dependent IGC mechanism has been studied in this paper. In this mechanism, IGC is induced by the dissolution of grain boundary (GB) precipitates of themselves.<BR>It was confirmed that the IGC mechanism played an important role mainly in the transpassive state corrosion potential region above about 1.2V(SHE), where neither the Cr depleted zone nor the segregation of P at GB induced IGC. The film-like and amorphous Ni-P compound, [Ni (Fe, Cr)]3P2 was found to precipitate at GB in Type 304 SS and to cause very thin but very deep IGC. Also, intermetallic compounds of Laves and χ phases were identified to precipitate at GB and to induce severe IGC due to the dissolution of themselves in Type 316 SS.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 79 (6), 713-720, 1993
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205182878848
-
- NII論文ID
- 110001493511
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
- http://id.crossref.org/issn/00211575
-
- NDL書誌ID
- 3826961
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可