- Temperature Rise and Deformation Behaviors of Materials during Fatigue Tests at Cryogenic Temperatures
- キョクテイオン クリカエシ オウリョクカ デ ノ キンゾク ザイリョウ ノ オ
この論文をさがす
抄録
Measurements and discussions were made on the temperature rise of specimen during fatigue tests at 4K. In SUS310S stainless steels and tension-tension (R=0.01) tests, temperature rise was negligible under the stress of the proof stress even at 10 Hz. In tension-compression (R=-1) tests, however, a hundred times of the temperature rise occurred compared with those at R=0.01. In SUS304L steel, which has low proof stress but the work hardening accompanied by the stress-induced martensitic transformation occurs in low temperatures, the temperature rise was rather small compared with SUS310S steels. The difference in the magnitude of the temperature rise especially between at R=0.01 and at R=-1 depended on the magnitude of the plastic deformation. The upper limit of the fatigue frequency (temperature rise<1K) was, which also varied with the applied stress and materials, 5Hz at R=0.01 and 0.1 Hz at R=-1.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 73 (1), 160-166, 1987
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205183052288
-
- NII論文ID
- 110001491813
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 3120294
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可