- Effect of Si on the Strength and the Toughness of Boron Treated Cr-Mo-Nb Steels
- ボロン処理したCr-Mo-Nb鋼の強度・靭性に及ぼすSiの影響
- ボロン ショリシタ Cr Mo Nb コウ ノ キョウド ジンセイ ニ オヨボ
この論文をさがす
抄録
Effect of Si content on the various mechanical properties and microstructures in B-treated Cr-Mo-Nb steels has been investigated.<BR>1) By increasing Si content, Charpy transition temperature of shear area (vTrsraises due to solution hardening and coarsening of austenite grain size, when coarse boro-carbides are not formed along grain boundaries during tempering treatment at high temperature.<BR>2) Si suppresses the coarsening of intergranular boro-carbides in case of high temperature tempering. As a result, in a steel containing excess dissolved B and so having boro-carbides along grain boundaries, it is considered that Si does not change vTrs spite of solution hardening and coarsening of austenite grain size due to increase of Si content.<BR>3) In an as quenched condition, austenite grain boundaries in a low Si content steel are clearly revealed, but those in a high Si content steel are not clearly observed after conventional etching. Consequently, it is considered that Si affects the grain boundary segregation.
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 73 (1), 199-206, 1987
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205183055744
-
- NII論文ID
- 110001491818
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 3120383
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可